Polydopamine-mediated synthesis of Si@carbon@graphene aerogels for enhanced lithium storage with lon
The application of Si as the anode materials for lithium-ion batteries (LIBs) is still severely hindered by the rapid ca......
The cycle life of oxygen carrier (OC) is crucial to the practical applications of chemical looping combustion (CLC).Cycl......
分别采用悬浮熔炼和单辊快淬的方法制备了晶粒尺寸为微米和纳米级的Mm(NiCoMnAl)5型贮氢合金粉体.与传统的微米级贮氢合金相比,纳......
Supersaturated bridge-sulfur and vanadium co-doped MoS2 nanosheet arrays with enhanced sodium storag
The low specific capacity and sluggish electrochemical reaction kinetics greatly block the development of sodium-ion bat......
Effect of the lead deposition on the performance of the negative electrode in an aqueous lead-carbon
Lead-carbon hybrid capacitors are the electrochemical devices between supercapacitors and lead-acid batteries,with low p......
ＭｌＮｉ４Ａｌ和ＭｌＮｉ４Ｍｎ贮氢电极性能的研究＊赵东江马松艳（绥化师专化学系绥化１５２０６１）关键词贮氢电极循环寿命自放电中图分类号Ｏ６４６．５４镍／氢化物（Ｎｉ／ＭＨ）二次电池以其洁净、安全、......
采用正交试验方法研究了ＭＨ－Ｎｉ电极的配方，导电剂，添加剂，制片压力，粘结剂等夺种工艺因素对电池循环寿命的影响，并探讨了负极配方，充放电制度，电......
研制成功３０Ａｈ实用型单体钠硫电池，研究了电池的性能特征和寿命，该电池具有放电电流大容量大，比能量大，放电容量与放电率无关，安全可靠等特点......
循环寿命是MH－Ni电池的重要指标之一。从材料的角度综述了MH－Ni电池循环寿命下降的原因，指出负极贮氢合金性能的衰减、正极氢氧化镍性......
分析了ＭＨ－Ｎｉ电池内压产生的原因。为了降低ＭＨ－Ｎｉ电池的内压提高寿命，分别通过ＭＨ负极用粘合剂以及合金粉制作工艺两个方面进行研究，结果表明，不同种......
综述了富液式铅酸蓄电池和VRLA电池对隔板的不同需求，详细列举了VRLA电地隔板提出的新要求；根据铅酸蓄电池应用领域的不同，包括启动、......
研究了采用尼龙纤维和聚丙类纤维混抄制备隔膜对ＭＨ－Ｎｉ电池放电容量和循环寿命的影响。结果表明：新研制隔膜的吸碱率和面电阻得到较大改善......
利用化学模式识别方法对不同电极制备工艺条件的ＭＨ－Ｎｉ电池的放电量和循环寿命进行了分析，并得出了提高电池相应性能的判据。对于放电容量......
研究了贮氢电池活化工艺与电池初始容量、充放电比率、电池极化、循环寿命之间的关系.结果表明:在设计贮氢合金时适当添加预防裂纹......
中间相碳球微球是一种常用的锂离子蓄电池负极材料。文中就其粒度及其分布对电池性能的影响加以研究讨论。将ＭＣＭＢ按粒度与分布分成五组......